Base Material: | Fibre Glass Coated PTFE | Layer Count: | 1 Layer, 2 Layers And Multi-layer |
---|---|---|---|
PCB Thickness: | 0.25mm, 0.5mm, 0.8mm, 1.0mm, 1.5mm, 2.0mm,3.0mm, 4.0mm, 5.0mm, 6.0mm, 8.0mm, 10.0mm, 12.0mm | PCB Size: | ≤400mm X 500mm |
Solder Mask: | Green, Black, Blue, Yellow, Red Etc. | Copper Weight: | 0.5oz (17 µm), 1oz (35µm), 2oz (70µm), 3oz (105µm) |
Surface Finish: | Bare Copper, HASL, ENIG, Silver, OSP,etc. | ||
High Light: | 1.6mm Teflon PCB Board,PTFE DK2.65 Teflon PCB Board,1.6mm PCB Printed Circuit Board |
PTFE High Frequency PCB Built on DK2.65 1.6mmTeflon With Immersion Gold for Couplers
Polytetrafluoroethylene (Short for PTFE), commonly known as "plastic king ", is a polymer compound made of tetrafluoroethylene by polymerization. It has excellent chemical stability, corrosion resistance, sealing, high lubrication and non-viscosity, electrical insulation and good aging resistance. Used as engineering plastic, it can be made into PTFE tube, rod, belt, plate, film and so on. Generally it’s used in high performance requirements of corrosion-resistant pipes, containers, pumps, valves as well as radar, high-frequency communication equipment, radio equipment.
Excellent performance:
F4BM-1/2 High Frequency PCB
F4BM-1/2 is laminated by laying up of varnished glass cloth with Teflon resin, according to the scientific formulation and strict technology process. This product takes some advantages over F4B series in the electrical performance(wider range of dielectric constant,lower dielectric loss angle tangent,increased resistance,and more stability of performance)
At RF and Microwave frequencies, the dielectric constant of PTFE materials is as low as 3.5 or below, which keeps strong signal during transmission across PCB, making them ideal for overcoming the high speed limitation of FR-4.
PCB Capability (PTFE)
PCB Material: | Fibre glass coated PTFE |
Code: | F4BM-1/2 (family series) |
Dielectric constant: | 2.2, 2.55, 2.65, |
3.0 and 3.5 | |
Layer count: | 1 Layer, 2 Layers and multi-layer |
Copper weight: | 0.5oz (17 µm), 1oz (35µm), 2oz (70µm), 3oz (105µm) |
PCB thickness: | 0.25mm, 0.5mm, 0.8mm, 1.0mm, 1.5mm, 2.0mm,3.0mm, 4.0mm, 5.0mm, 6.0mm, 8.0mm, 10.0mm, 12.0mm |
PCB size: | ≤400mm X 500mm |
Solder mask: | Green, Black, Blue, Yellow, Red etc. |
Surface finish: | Bare copper, HASL, ENIG, Silver, OSP,etc. |
Data Sheet of F4B (PTFE)
Name | Test condition | Unit | Value | |||
Density | Normal state | g/ cm3 | 2.1~2.35 | |||
Moisture Absorption | Dip in the distilled water of 20±2℃ for 24 hours | % | ≤0.02 | |||
Operating Temperature | High-low temperature chamber | ℃ | -50℃~+260℃ | |||
Thermal Conductivity | W/m/k | 0.8 | ||||
CTE (typical) | 0~100℃ (εr :2.1~2.3) | ppm/℃ | 25(x) | |||
34(y) | ||||||
252(z) | ||||||
CTE (typical) | 0~100℃ (εr :2.3~2.9) | ppm/℃ | 14(x) | |||
21(y) | ||||||
173(z) | ||||||
CTE (typical) | 0~100℃ (εr :2.9~3.5) | ppm/℃ | 12(x) | |||
15(y) | ||||||
95(z) | ||||||
Shrinkage Factor | 2 hours in boiling water | % | 0.0002 | |||
Surface Resistivity | 500V DC | Normal state | M·Ω | ≥1×104 | ||
Constant humidity and temperature | ≥1×103 | |||||
Volume Resistivity | Normal state | MΩ.cm | ≥1×106 | |||
Constant humidity and temperature | ≥1×105 | |||||
Pin Resistance | 500V DC | Normal state | MΩ | ≥1×105 | ||
Constant humidity and temperature | ≥1×103 | |||||
Surface dielectric strength | Normal state | d=1mm(Kv/mm) | ≥1.2 | |||
Constant humidity and temperature | ≥1.1 | |||||
Dielectric Constant | 10GHZ | εr | 2.20,2.55,2.65,3.0,3.5 (±2%) | |||
Dissipation Factor | 10GHZ | tgδ | 2.2 | ≤7×10-4 | ||
2.55~2.65 | ≤1×10-3 | |||||
3.0~3.5 | ≤1.5×10-3 |
4 Layer 2oz RO4003C Multi Layer PCB High Frequency For Automotive Radar
Microwave Rogers RT / Duroid 6010LM Rogers PCB Board ceramic PTFE composites
Rogers RT/Duroid 5880 PCB High Frequency 15mil 1 Oz Copper PCB For Millimeter Wave Applications
Customized PCB 32mil Rogers 0.813mm RO4003C Double Sided RF PCB
Dual Layer Flexible PCB Built on Polyimide With Immersion Gold and PI Stiffener
1 Layer PI Material Flexible PCB Board No Peelable Coverlay
2 Layer Flexible PCB Built On Polyimide with Stiffener On the Tail for Tablet Computer Battery
High Frequency PCB Built On 1.5mm Dual Layer PTFE (Teflon) Heavy Copper Circuit Boards
HASL Lead Free 1up PTFE PCB Board 1.5mm PTFE Plate
DK2.65 PTFE Double Sided With OSP and Green Mask for Combiners High Frequancy Circuit Board
F4B High Frequency PCB Built On 3.0mm RF PCB Board for Patch Antenna