Product Details:
Payment & Shipping Terms:
|
Base Material: | PTFE | PCB Thickness: | 1.6mm |
---|---|---|---|
Copper Weight: | 0.5 Oz | Layer Count: | 2 Layers |
Solder Mask: | Gloss Green | PCB Size: | 89 X 61mm=1PCS |
Surface Finish: | OSP | ||
Highlight: | PTFE High Frequency Printed Circuit Board,0.5 Oz High Frequency Printed Circuit Board,0.5 Oz High Frequency PCB |
High Frequency PCB On DK2.65 PTFE Double Sided With OSP and Green Mask for Combiners
(Printed Circuit Boards are custom-made products, the picture and parameters shown are just for reference)
Polytetrafluoroethylene (Short for PTFE), commonly known as "plastic king ", is a polymer compound made of tetrafluoroethylene by polymerization. It has excellent chemical stability, corrosion resistance, sealing, high lubrication and non-viscosity, electrical insulation and good aging resistance. Used as engineering plastic, it can be made into PTFE tube, rod, belt, plate, film and so on. Generally it’s used in high performance requirements of corrosion-resistant pipes, containers, pumps, valves as well as radar, high-frequency communication equipment, radio equipment.
Polytetrafluoroethylene (F4,PTFE) has a series of excellent performance:
1.high temperature resistance: long-term use temperature 200~260 degrees Celsius.
2.low temperature resistance: still soft at -100 degrees Celsius;
3.corrosion resistance: resistant aqua regia and all organic solvents;
4.climate resistance: best aging life in plastics;
5.high lubrication: with the smallest friction coefficient in plastics (0.04);
6.Non-viscous: with minimal surface tension in solid materials without adhering to any substance;
7.non-toxic: with physiological inertness;
8.excellent electrical properties, ideal for C class of insulating materials, a thick layer of stack of newspaper can block 1500 V of high voltage;
9.smoother than ice.
F4BM-1/2 is laminated by laying up of varnished glass cloth with Teflon resin, according to the scientific formulation and strict technology process. This product takes some advantages over F4B series in the electrical performance(wider range of dielectric constant,lower dielectric loss angle tangent,increased resistance,and more stability of performance)
At RF and Microwave frequencies, the dielectric constant of PTFE materials is as low as 3.5 or below, which keeps strong signal during transmission across PCB, making them ideal for overcoming the high speed limitation of FR-4.
Our PCB Capability
PCB Material: | Fibre glass coated PTFE |
Code: | F4BM-1/2 (family series) |
Dielectric constant: | 2.2, 2.55, 2.65, 3.0 and 3.5 |
Layer count: | 1 Layer, 2 Layers and multi-layer |
Copper weight: | 0.5oz (17 µm), 1oz (35µm), 2oz (70µm), 3oz (105µm) |
PCB thickness: | 0.25mm, 0.5mm, 0.8mm, 1.0mm, 1.5mm, 2.0mm, 3.0mm, 4.0mm, 5.0mm, 6.0mm, 8.0mm, 10.0mm, 12.0mm |
PCB size: | ≤400mm X 500mm |
Solder mask: | Green, Black, Blue, Yellow, Red etc. |
Surface finish: | Bare copper, HASL, ENIG, Silver, OSP,etc. |
PCB Specifications
PCB SIZE | 89 x 61mm=1PCS |
BOARD TYPE | Microwave PCB |
Number of Layers | Double sided PCB |
Surface Mount Components | NO |
Through Hole Components | YES |
LAYER STACKUP | copper ------- 18um(0.5oz)+PLATE |
PTFE 1.5mm | |
copper ------- 18um(0.5oz)+PLATE | |
TECHNOLOGY | |
Minimum Trace and Space: | 6mil/9mil |
Minimum / Maximum Holes: | 0.9/2.3mm |
Number of Different Holes: | 3 |
Number of Drill Holes: | 156 |
Number of Milled Slots: | 0 |
Number of Internal Cutouts: | 1 |
Impedance Control | no |
BOARD MATERIAL | |
Glass Epoxy: | PTFE ER= 2.55 |
Final foil external: | 1oz |
Final foil internal: | 1oz |
Final height of PCB: | 1.6 mm ±0.16 |
PLATING AND COATING | |
Surface Finish | OSP, Thickness >0.2µm |
Solder Mask Apply To: | TOP, 12micron Minimum |
Solder Mask Color: | Gloss Green, Taiyo PSR-2000GT600D |
Solder Mask Type: | LPSM |
CONTOUR/CUTTING | Routing |
MARKING | |
Side of Component Legend | No silkscreen required. |
Colour of Component Legend | No silkscreen required. |
Manufacturer Name or Logo: | No silkscreen required. |
VIA | Plated through hole(PTH), via open. |
FLAMIBILITY RATING | UL 94-V0 Approval MIN. |
DIMENSION TOLERANCE | |
Outline dimension: | 0.0059" |
Board plating: | 0.0029" |
Drill tolerance: | 0.002" |
TEST | 100% Electrical Test prior shipment |
TYPE OF ARTWORK TO BE SUPPLIED | email file, Gerber RS-274-X, PCBDOC etc |
SERVICE AREA | Worldwide, Globally. |
Electrical properties of F4B PTFE
Name | Test condition | Unit | Value | |||
Density | Normal state | g/ cm3 | 2.1~2.35 | |||
Moisture Absorption | Dip in the distilled water of 20±2℃ for 24 hours | % | ≤0.02 | |||
Operating Temperature | High-low temperature chamber | ℃ | -50℃~+260℃ | |||
Thermal Conductivity | W/m/k | 0.8 | ||||
CTE (typical) | 0~100℃ (εr :2.1~2.3) | ppm/℃ | 25(x) | |||
34(y) | ||||||
252(z) | ||||||
CTE (typical) | 0~100℃ (εr :2.3~2.9) | ppm/℃ | 14(x) | |||
21(y) | ||||||
173(z) | ||||||
CTE (typical) | 0~100℃ (εr :2.9~3.5) | ppm/℃ | 12(x) | |||
15(y) | ||||||
95(z) | ||||||
Shrinkage Factor | 2 hours in boiling water | % | 0.0002 | |||
Surface Resistivity | 500V DC | Normal state | M·Ω | ≥1×104 | ||
Constant humidity and temperature | ≥1×103 | |||||
Volume Resistivity | Normal state | MΩ.cm | ≥1×106 | |||
Constant humidity and temperature | ≥1×105 | |||||
Pin Resistance | 500V DC | Normal state | MΩ | ≥1×105 | ||
Constant humidity and temperature | ≥1×103 | |||||
Surface dielectric strength | Normal state | d=1mm(Kv/mm) | ≥1.2 | |||
Constant humidity and temperature | ≥1.1 | |||||
Dielectric Constant | 10GHZ | εr | 2.20,2.55,2.65,3.0,3.5 | |||
(±2%) | ||||||
Dissipation Factor | 10GHZ | tgδ | 2.2 | ≤7×10-4 | ||
2.55~2.65 | ≤1×10-3 | |||||
3.0~3.5 | ≤1.5×10-3 |